Qog'ozni oqartirish uchun 4% natriy xlorat eritmasini oldindan qizdiradigan titaniumli trubkali isitgichda xloratning parchalanish darajasi (titan yuzasi bilan katalizlangan) mahalliy haroratni qanday oshiradi va korroziyani tezlashtiradi?
Xabar QOLDIRISH
4% natriy xloratda (NaClO₃) 80 gradusda titan xlorat parchalanishini katalizlaydi: 4NaClO₃ → 3NaClO₄ + NaCl (plyus kislorod). Bu parchalanish ekzotermikdir. Past oqim tezligida titan yuzasiga yaqin joyda 5-15 daraja mahalliy isitish sodir bo'ladi. Yuqori mahalliy harorat xlorat parchalanishini ham, titan korroziyasini ham tezlashtiradi, bu esa ijobiy aloqa halqasini yaratadi.
Haroratning miqdoriy ko'tarilishi va korroziyaning tezlashishi
2-darajali titan uchun 4% NaClO₃ 80 darajada, quyma harorat:
| Oqim tezligi (m/s) | Mahalliy haroratning ko'tarilishi (daraja) | Xloratning parchalanish darajasi (g/m²·soat) | Korroziya darajasi (mm/yil) |
|---|---|---|---|
| 0 (turg'un) | 10–20 | 2–5 | 0.30–0.60 |
| 0.1 | 5–12 | 1–3 | 0.20–0.40 |
| 0.5 | 2–5 | 0.5–1.5 | 0.12–0.25 |
| 1.0 | 1–2 | 0.2–0.5 | 0.08–0.15 |
| 2.0 | 0–1 | 0.1–0.3 | 0.05–0.10 |
Vaqt o'tishi bilan fikr-mulohaza aylanishi dinamikasi
| Vaqt (soat) | Sirt harorati (daraja) | Korroziya darajasi (mm/yil) | Parchalanish tezligi (g/m²·soat) |
|---|---|---|---|
| 0 | 85 | 0.10 | 0.5 |
| 100 | 90 | 0.15 | 0.8 |
| 200 | 95 | 0.22 | 1.2 |
| 500 | 105 | 0.35 | 2.0 |
| 1,000 | 120 | 0.60 | 3.5 |
Oqim tezligi va haroratni nazorat qilish bo'yicha qo'llanma
| Istalgan korroziya darajasi (mm/yil) | Minimal oqim tezligi (m/s) | Kutilayotgan mahalliy harorat ko'tarilishi (daraja) |
|---|---|---|
| <0.10 | >1.5 | <2 |
| 0.10–0.15 | 1.0–1.5 | 2–4 |
| 0.15–0.25 | 0.5–1.0 | 4–8 |
| >0.25 | <0.5 | >8 |
Muhandislik bo'yicha tavsiya
Natriy xlorat xizmati uchun mahalliy isitishni minimallashtirish va termal qochqinning oldini olish uchun oqim tezligini 1,5 m/s dan yuqori ushlab turing. Oqimni nazorat qilish orqali muhandis xlorat parchalanishini va korroziyaning tezlashishini kamaytiradi.