347 isitish moslamasi trubkasidagi ortiqcha niobiydan (0,60-0,80 og'irlikda) birlamchi MC karbidlarining (NbC/TiC) hajm ulushi 80 gradusdagi 1000 ppm xloridli suvda chuqurni boshlash joyining zichligi va teshilish vaqtini qanday boshqaradi

Xlorid xizmatidan oshib ketish-barqarorlik uchun jarima

For sheathed electric heating tubes of 347 stainless steel (Nb-stabilized) in moderate chloride water (1,000 ppm Cl⁻) at 80°C, the excess niobium beyond the stoichiometric requirement for carbon fixation (Nb:C ratio >10:1) leads to the formation of primary MC carbides (NbC) not dissolved during solution annealing. The initial carbides are usually 2-10 m in size and are cathodic sites for pit start. At 0.30-0.40 wt % niobium (Nb:C = 8:1 to 10:1) principal MC volume percentage is 0.04-0.06% and service life >10 yil. Birlamchi MC hajm ulushi 0,12-0,20% gacha ko'tariladi (ortiqcha barqarorlashgan (0,60-0,80 og'irlikdagi niobiy)) Chuqur zichligi 5-10 marta ortadi Teshilish vaqti 2-4 yilgacha kamayadi. 80 daraja haroratda 1000 ppm Cl⁻ suv.

Birlamchi MC karbid tomonidan boshqariladigan chuqurchalar mexanizmi

347 zanglamaydigan po'latdan qotish jarayonida birlamchi MC karbidlari (NbC, TiC) hosil bo'ladi. Yuqori elektr o'tkazuvchanligi va olijanob sirt sifatlari tufayli ular ostenitik matritsa uchun katoddir. Agar niobiy miqdori og'irligi 0,45-0,50% dan yuqori bo'lsa (oddiy uglerod miqdori 0,04-0,06%), to'liq stabilizatsiya uchun zarur bo'lgan miqdordan ortiq bo'lgan har qanday qo'shimcha niobiy ko'proq birlamchi karbidlarning hosil bo'lishiga olib keladi. Bu zarrachalar eritmani yumshatishda (1050-1100 daraja) erimaydi va oxirgi quvurda saqlanadi. Xlorid eritmalarida bu karbidlar katodik kislorodni qaytarish reaktsiyasida ishtirok etishlari va atrofdagi matritsaning anodik erishini ta'minlaydigan galvanik juftlikni hosil qilishlari ma'qul. Chuqurning boshlanishining zichligi sirtda ta'sirlangan asosiy MC karbid zarralari soniga mutanosibdir.

Haddan tashqari niobiy, MC hajmi fraktsiyasi va pitting ishlashi o'rtasidagi bog'liqlik

Har xil niobiy darajalariga ega 347 trubka bilan boshqariladigan immersion sinovlari (doimiy uglerod 0,05-0,06%, titanium)<0.01%) in 1,000 ppm Cl- water (pH 7.0, aerated) at 80°C for 5,000 hours have established the following pit initiation densities and perforation times.

Niobiy (wt%) Nb:C nisbati Uglerod (wt%) MC Birlamchi hajmli fraksiya (%)MC zarrachalar hajmi (mkm) 5000 soatdan keyin chuqur zichligi (chuqurlar/sm2) 5000 soatdan keyin maksimal chuqur chuqurligi (mkm) Teshilish vaqti (1,5 mm devor, yillar davomida) 80m00 Cl- Xizmat 0.20 4:1 0.05 0.02-0.03 1-2 0.2-0.5 15-25 10-15 Qabul qilinadi (barqaror-barqaror, sezgirlik xavfi ostida)
0.30 6:1 0.05 0.03-0.04 1-2 0.3-0.6 18-28 9-12 Qabul qilinadi 0.35 7:1 0.05 0.04-0.05 1-2 0.5-1.0 20-35 8-11 Qabul qilinadi 0.40 8:1 0.05 0.05-0.06 1-3 0.8-1.5 25-40 6-9 Qabul qilinadi (optimal balans) 0.45 9:1 0.05 0.06-0.08 2-4 1-2 30-50 5-7 Marginal 0.50 10:1 0.05 0.08-0.10 2-5 2-3 40-60 4-5 Tavsiya etilmaydi 0.60 12:1 0.05 0.12-0.15 3-6 4-8 50-80 2.5-4 Yo‘q 0.70 14:1 0.05 0.12-0.15 3-6 4-8 50-80 2.5-4 Yo‘q 0.70 14}:1{12}}: Yo‘q 0.70 14:1{1} 1.00 20:1 0.05 0.25-0.30 6-12 25-40 100-150 0.8-1.2 Yo‘q
Eritmaning tavlanish haroratining birlamchi MC erishiga ta'siri

Yuqori eritmaning tavlanish harorati birlamchi MC karbidlarini qisman eritishi mumkin, ammo 1150 darajadan ortiq donning qo'pollashishi va ferrit hosil bo'lishi xavfi mavjud.

Eritmani yumshatish harorati (daraja) 0,60% Nb (%) MC zarracha hajmi (mkm) Chuqur zichligi (chuqurlik/sm2) Tavsiya etilgan 1,050 0.12-0.15 3-6 4-8 No 1,080 0.10-0.12 3-5 3-6 Yo‘q 1,100 0.08-0.10 3-4 2-4 Chek 1,{9}} o‘sishi mumkin
1,150 0.05-0.07 2-3 1-2 Qabul qilinadi (donning kattalashishi → pastroq emirilish kuchi)
347 Xlorid xizmati bo'yicha amaliy tavsiyalar

Kerakli xizmat muddati (yillar) Maksimal niobiy (og'irligi%) Minimal eritma tavlanish harorati (oC) Maksimal birlamchi MC Vol. Fraksiya (%)Barqarorlik tavsiya etiladi10 0.40 1,050 0.06 Yo'q (eritma tavlanishi)
8-10 0.42 1,060 0.07 Yo'q 5-8 0.45 1,080 0.08 Yo'q (Barqarorlashdan saqlaning)
3-5 0.50 1,100 (don hajmini sozlash bilan) 0,10 Marginal<3 >0.50Not recommended >0.10 316L yoki dupleks 2205 MC karbid tarkibini tekshirishga yangilang

Ba'zi chuqurliklarga qarshilik talab qiladigan iste'molchilar uchun tekshirishning ikki yo'li mavjud. Birinchisi, sayqallangan va biroz o'yilgan kesmaning SEM metallografik tekshiruvi. Birlamchi MC karbidlarini (burchakli, 2–10 mkm) 1000× Qabul qilishda hisoblang:<5 particles/mm2 for >8 yillik hayot